CERTIFICATES PARIEK

Average mass loss value 370 mg. with a CS 10 type grinding wheel loaded with 10 N
Average mass loss value 442 mg. with a CS 17 type grinding wheel loaded with 10 N
Average mass loss value 472 mg. with a CS 22 type grinding wheel loaded with 10 N
Average mass loss value 546 mg. with a CS 18 type grinding wheel loaded with 10 N 

Average flezing resistance value 2,17 N/mm²

10% thickness reduction = 104,58 kN del 20% thickness reduction = 173,40 kN
10% thickness reduction = 96,60 kN del 20% thickness reduction = 170,10 kN
10% thickness reduction = 80,10 kN del 20% thickness reduction = 155,37 kN
Flaw load = 236,40 kN Collapse load 303,54 kN
Flaw load 228,12 kN Collapse load 295,80 kN
Flaw load 228,12 kN Collapse load 256,26 kN

Average penetration value 1,08 mm. 

Average penetration value 1,355 mm.

Average penetration value 1,075 mm

Dry leather sliding item 0,585
Rubber sliding item on wet floor 0,78 

First direction +0,178 -0,666 -0,079
Second direction  -0,477 +1,113 +0,154
First direction +0,596 +1,067 -0,436
Second direction +0,584 -0,499 -0,651

Average residual imprint value 0,52 mm

Lambda 0,141 W/(mK)

Temperature 21° Humidity 30%
(Measurement 1) > 5 x 10 ¹¹ Ohm;
(Measurement 2) > 3 x 10 ¹¹ Ohm
(Measurement 3) > 3 x 10 ¹¹ Ohm

(Measurement 1) > 5 x 10 ¹¹ Ohm;
(Measurement 2) > 3 x 10 ¹¹ Ohm;
(Measurement 3) > 3 x 10 ¹¹ Ohm;

Method CSE RF 2/75/A: Assigned category: first
Method CSE RF 3/77 : Assigned category: first
On the basis of above mentioned tests, pursuant to Ministerial Decree 26/6/84, the material may be assigned to fire reaction class 1(one): homologation number TO1332B41CD100001 of 17/9/97.(File. 4190 sub. 1702).